Ultra Şeffaf Zirkonya Seramikleri
Apr 22, 2022
Malzeme tanıtımı
If the content of yttrium oxide as stabilizer is appropriately increased (5 mol percent ) in zirconia ceramics, the cubic phase zirconia crystal becomes the main crystal phase of the zirconia material, so the semi-permeability is very good, so it is called "super permeable oxide". zirconium". At the same time, due to its low content of tetragonal zirconia crystals, lack of phase transformation toughening mechanism, low strength and toughness, less phase transformation occurs in the entire temperature range of sintering and cooling, and the material has almost no volume change. It is called "fully stabilized zirconia".
2015'te piyasaya sürülen ultra{{0}}tamamen şeffaf zirkonya-seramik malzeme, dengeleyici olarak yüzde 5 mol (ağırlıkça yüzde 912) itriya kullanır (5Y- TZP) ve alümina içeriği ağırlıkça yüzde 0,05'ten az veya neredeyse hiç ilave yok ve kübik faz oksidasyonu Zirkonyum kristalinin içeriği yüzde 70'ten fazla, tetragonal fazın içeriği yüzde 30'dan az, yarı {{11 }}malzemenin geçirgenliği çok yüksektir ve süper-şeffaf performans elde edilir (çalışmalar, 1.0 mm kalınlığa sahip ultra-şeffaf zirkonyanın TP değerinin 35'ten fazla olduğunu göstermektedir), ve genel eğilme mukavemeti Yaklaşık 500600 MPa, kırılma tokluğu 2.22.7 MPa.m1/2.
Klinik Uygulama
Dördüncü-nesil zirkonyanın yarı geçirgenliği-seramik malzemenin yarı geçirgenliği, lityum disilikat cam seramiklerinkine neredeyse yakındır ve estetiği çok iyidir, ancak gücü daha iyidir. cam seramiklerdendir. Çoğunlukla ön dişlerin tek kron ve kaplama restorasyonu için kullanılır.